According to thickness

Hastelloy^® X

ASTM B435, B366, B572, B619 B622, B626, B751, B775, B829
UNS Number N06002
DIN 2.4665

Other common names: Alloy X, Inconel® HX

Hastelloy X is a nickel-chromium-iron-molybdenum superalloy with outstanding high temperature strength, oxidation resistance, and fabricability. Alloy X’s oxidation resistance is excellent up to 2200° F. This nickel steel alloy has also been found to be exceptionally resistant to stress-corrosion cracking in petrochemical applications. Matrix stiffening provided by the molybdenum content results in high strength in a solid-solution alloy having good fabrication characteristics. Although this nickel alloy is primarily noted for heat and oxidation resistance it also has good resistance to chloride stress-corrosion cracking, carburization, and excellent resistance to reducing or carburizing atmospheres. Two common conditions that often lead to early failure in high temperature alloys, carburization and nitriding, Hastelloy X resists.

In what forms is Hastelloy X Available at Mega Mex?

• Sheet
• Plate
• Bar

What are the characteristics of Hastelloy X?

• Outstanding oxidation resistance through 2000° F
• Resistant to carburization and nitriding
• Excellent high temperature strength
• Good resistance to chloride stress-corrosion cracking

Chemical Composition, %

Ni	Mo	Cr	Fe	W	Co	Mn	C
Remainder	8.0-10.0	20.5-23.0	17.0-20.0	.2-1.0	.5-2.5	1.0 max	.05-.15
P	S	Si	Al	Ti	B	Cu
.04 max	.03 max	1.0 max	.50 max	.15 max	.01 max	.50 max

In what applications is Hastelloy X used?

• Gas turbines
• Petrochemical industry
• Industrial furnaces
• Heat treating equipment
• Nuclear engineering
• Jet engine combustion chambers
• Aircraft cabin heaters
• Turbine exhaust components

Alloy X is one of the most widely used nickel base superalloys for gas turbine engine combustion zone components such as transition ducts, combustor cans, spray bars and flame holders as well as in afterburners, tailpipes and cabin heaters. It is recommended for use in industrial furnace applications because it has unusual resistance to oxidizing, reducing and neutral atmospheres. Hastelloy X is also used in the chemical process industry for retorts, muffles, catalysts support grids, furnace baffles, tubing for pyrolysis operations and flash drier components.

Fabrication with Hastelloy X

Alloy X has excellent forming and welding characteristics. It can be forged and, because of its good ductility, can be cold worked. It can be welded by both manual and automatic methods including shielded metal arc, gas tungsten arc, gas metal arc and submerged arc processes. The alloy can also be resistance welded. For hot forming, the alloy should be heated to a starting temperature of 2150° F (1175°C).

ASTM Specifications

Sheet/Plate	Bar
B435	B572

Mechanical Properties
Representative Tensile Properties, sheet

Temp° F	Tensile (psi)	.2% Yield (psi)	Elongation in 2” %
70	110,600	54,900	44
1000	89,000	35,600	49
1200	83,000	35,400	54
1400	67,000	34,400	53
1600	45,000	28,200	58